MARK3 EverCem PLUS Universal Resin Cement

MARK3 EverCem PLUS universal, dual cure resin cement for indirect restorations made from ceramics, composites, or metal, as well as cementing posts. Its newly updated formula now contains MDP, which makes it a superior cement for zirconia restorations. This also means the pre-treatment of tooth surfaces, such as etching, priming, and bonding is unnecessary. In turn this reduce treatments steps and patient chair time.

Comparable to RelyX Ultimate, Kerr NX3, Panavia SA Universal, G-Cem One, and Premier ZR-Cem materials.

Product Details:

• Low film thickness (<0.3mm) ensures a closer fit of the restoration, while providing greater bonding values.
• New and Improved containing 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) making it a superior cement for zirconia restorations.
• Two functional monomers for perfect results
• Indications: All-ceramic crowns, inlays/onlays, all-metal or ceramic metal crowns/bridges, high-strength ceramic zirconia, crowns, and metal/fiber posts
• Contraindications: Ceramic veneers, crown or bridges with poor retention, and resin-bonded bridgges.
• Curing: Self-cure, light-cure, or dual-cure methods
• No need for etching or bonding.
• No need for refrigeration
• Easy to clean-up excess restorative material.
• Automix syringe style.
• Made in Isreal.

Physical Properties:

• Compressive Strength: 275-300 MPa
• Flexural Strength: 75-125 MPa
• Shear Bond Strength to Enamel: (Zirconia) 28-32 MPa
• Particle size: 0.02 μm-20 μm (inorganic filler ~40%)
• Film thickness: 12 μm
• Working time: 2-2.5 min
• Setting time: 3 min 15 secs
• Adhesion to dentin (self cure): 22 mPa
• Adhesion of zirconium oxide to dentin (self cure): 18 mPa
• Zirconium oxide on dentin (dual cure): 28 mPa
• Adhesion to zirconium oxide (self cure): 25 mPa
• Shade: Universal

Includes: 8 mL automix syringe of MARK3 EverCem Cement and 6 mixing tips.